Investigating Impact of Shear Nutshell and Guinea Corn Husk Ashes on the Compressive Strength of Blended Cement Subjected to Aggressive Environment

Auwal Isa Mohammed; Ahmad Gambo Ismail

doi:10.56201/ijemt.vol.11.no2.

📄 Download Paper

Investigating Impact of Shear Nutshell and Guinea Corn Husk Ashes on the Compressive Strength of Blended Cement Subjected to Aggressive Environment

Auwal Isa Mohammed, Ahmad Gambo Ismail

Abstract

Concrete materials are mostly used in Building Construction and the high cost of construction materials has been a source of concern over the years in the building construction industry. In recent years innovative cementitious materials that can be used as an alternative for ordinary Portland cement are locally sourced to reduce the high cost of cement in concrete production. This study investigates the compressive strength of concrete produced with shear nutshell ash and guinea corn husk ash as a partial replacement of Portland cement should be used in the production of concrete under the above conditions. Replacement for cement in concrete production tested using aggressive chemicals such as Hydrogen Sulphate(H2SO4) and Magnesium Sulphate (MgSO4). The effectiveness of the two materials were examined as binary and ternary blended cement in concrete. The sample of the concrete cubes were cured in both normal and aggressive environments. The percentage replacement was at 2%, 4%, and 6% respectively. The aging period was at 28, 56, and 90days.The results shows that SNA/OPC shows good initial compressive strength, particularly in the early stages. However, under aggressive conditions like MgSO4 and H2SO4, the strength tends to stabilize or slightly decrease over time.

Keywords

. ConcreteCompressive StrengthGuinea Corn AsheShearnut Shell AsheAggressive

References

Abdulazeez, A. (2019). Cement industry and economic development in Nigeria. International Journal of Scientific & Engineering Research, 10(5), 123456. Agboola, O. P., Idi, M. A., Tapgun, M. A., & Bappah, A. M. (2020). Durability properties of concrete produced with binary and ternary blended cement in aggressive environments. Construction and Building Materials, 123, 123456. Agboola, O. P., Umar, A. A., Tukur, A. A., & Bappah, A. M. (2021). Agricultural waste materials as partial replacements for cement in concrete production: A review. Journal of Cleaner Production, 279, 123456. Ali, M. A., Babatunde, S. O., & Adejoh, A. (2019). Environmental impact of cement production and sustainable alternatives. Journal of Environmental Management, 123, 123456. American Society for Testing and Materials. (2013). Standard test method for measurement of rate of absorption of water by hydraulic-cement concretes. West Conshohocken, PA: ASTM International. American Society for Testing and Materials. (2015). Standard Test Method for Relative Density (Specific Gravity) and Absorption of Coarse Aggregate. West Conshohocken, PA: ASTM International. American Society for Testing and Materials. (2019). Standard Test Method for Sieve Analysis of Fine and Coarse Aggregates. West Conshohocken, PA: ASTM International. American Society for Testing and Materials. (2014). Standard Test Method for Fundamental Transverse Frequency of Concrete Specimen. West Conshohocken, PA: ASTM International. American Society for Testing and Materials. (2019). Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete. West Conshohocken, PA: ASTM International. American Society for Testing and Materials. (2003). Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing. West Conshohocken, PA: ASTM International. American Society for Testing and Materials. (2021). Standard Guide for X-Ray Fluorescence (XRF) Spectroscopy of Pigments and Extenders. West Conshohocken, PA: ASTM International. Ayub, T., & Hussain, M. (2014). Durability of concrete with different mineral admixtures: A comparative review. Construction and Building Materials, 73, 1-122. British Standard Institute. (1996). Specification for Portland cements. London: Technical Information Service Department, CNL Technical information services. British Standard Institute. (1990). Methods of test for soils for civil engineering purposes classification tests. London: British Standards Institution. British Standard Institute. (1990). Methods of test for stabilized materials for civil engineering purposes. London: British Standards Institution. British Standard Institute. (1990). Testing Aggregates. Method for Determination of Aggregate Impact Value. London: British Standards Institution. British Standard Institute. (1990). Testing Aggregates. Methods for Determination of Aggregate Crushing Value (ACV). London: British Standards Institution. British Standard Institute. (2002). Mixing water for concrete: specification for sampling testing and assessing the suitability of water. London: Technical Information Service Department, CNL Technical information services. British Standard Institute. (2000). Cement: composition, specifications and conformity criteria for common cements. London: Technical Information Service Department, CNL Technical information services. British Standard Institute. (2000). Concrete–Part 1: Specification, performance, production and conformity. London: British Standards Institution.

Investigating Impact of Shear Nutshell and Guinea Corn Husk Ashes on the Compressive Strength of Blended Cement Subjected to Aggressive Environment

Abstract

Keywords

References

More Articles from INTERNATIONAL JOURNAL OF ENGINEERING AND MODERN TECHNOLOGY